Grinding balls are usually made of materials with moderate hardness, wear resistance, and corrosion resistance, such as high manganese steel, aluminum oxide, silicon carbide, etc. It is refined through processes such as drawing, cutting, and grinding, with uniform particles and no internal pores, and has advantages such as long service life and short shot blasting time.
Specification:
Name | Steel wire cutting shot | |
Chemical composition | Carbon | 0.45~0.85% |
Manganese | 0.40~1.30% | |
Silicon | 0.10~0.35% | |
Sulfur | <0.05%,MAX | |
Phosphorus | <0.04%,MAX | |
Hardness (HRc) | 42 min | |
Density | 7.8g/cm3 min | |
Microstructure | ||
Grain Shape:
1) G1 (CCW): Single Conditioned (Slightly Rounded)
2) G2 (DCCW): Double Conditioned (Double Rounded)
3) G3 (SCCW): Spherically Conditioned
Grinding balls are usually made of materials with moderate hardness, wear resistance, and corrosion resistance, such as high manganese steel, aluminum oxide, silicon carbide, etc. It is refined through processes such as drawing, cutting, and grinding, with uniform particles and no internal pores, and has advantages such as long service life and short shot blasting time.
Specification:
Name | Steel wire cutting shot | |
Chemical composition | Carbon | 0.45~0.85% |
Manganese | 0.40~1.30% | |
Silicon | 0.10~0.35% | |
Sulfur | <0.05%,MAX | |
Phosphorus | <0.04%,MAX | |
Hardness (HRc) | 42 min | |
Density | 7.8g/cm3 min | |
Microstructure | ||
Grain Shape:
1) G1 (CCW): Single Conditioned (Slightly Rounded)
2) G2 (DCCW): Double Conditioned (Double Rounded)
3) G3 (SCCW): Spherically Conditioned