Manufactured from high quality steel wire cut into cylindrical, each particle size almost equal to its diameter, or round shape through conditioning process, its life longer and residues less than steel shot, it is widely used in cleaning of steel surfaces, cast steel product, descaling and rust removal, deburring and for shot peening to improve the stress-resistance of metal products.
Production standard:
SAE J1993/SAE J441, ISO11124-5, GB/T 18838.5
Specification:
Name | Steel wire cutting shot | |
Chemical composition | Carbon | 0.45~0.85% |
Manganese | 0.40~1.30% | |
Silicon | 0.10~0.35% | |
Sulfur | <0.05%,MAX | |
Phosphorus | <0.04%,MAX | |
Hardness (HRc) | 42 min | |
Density | 7.8g/cm3 min | |
Microstructure | ||
Applicable industry:
Desanding | Foundry/ Casting |
Descaling | Steel / Construction |
Shot Peening | Automotive / Aero |
Manufactured from high quality steel wire cut into cylindrical, each particle size almost equal to its diameter, or round shape through conditioning process, its life longer and residues less than steel shot, it is widely used in cleaning of steel surfaces, cast steel product, descaling and rust removal, deburring and for shot peening to improve the stress-resistance of metal products.
Production standard:
SAE J1993/SAE J441, ISO11124-5, GB/T 18838.5
Specification:
Name | Steel wire cutting shot | |
Chemical composition | Carbon | 0.45~0.85% |
Manganese | 0.40~1.30% | |
Silicon | 0.10~0.35% | |
Sulfur | <0.05%,MAX | |
Phosphorus | <0.04%,MAX | |
Hardness (HRc) | 42 min | |
Density | 7.8g/cm3 min | |
Microstructure | ||
Applicable industry:
Desanding | Foundry/ Casting |
Descaling | Steel / Construction |
Shot Peening | Automotive / Aero |